Influence of Sealer and Light-Curing Units on Push-Out Bond Strength Of Composite Resin to Weakened Roots

Abstract The aim of this study was to assess the influence of sealer and light-curing unit on regional bond strength of resin composite to the weakened roots. Ninety roots of incisors were experimentally weakened, subjected to biomechanical preparation and filled with either Endofill, AH Plus or MTA Fillapex The roots were desobturated e reinforced with resin composite and fiber post light-activated with one of the light sources: halogen at 600 mW/ cm2 (QTH-600), LED at 800 mW/ cm2 (LED-800) and LED at 1500 mW/ cm2 (LED-1500). The roots were sectioned in slices from cervical, middle and apical root-reinforcement regions and analyzed by push out test, scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Bond strength data were analyzed using three-way ANOVA and Tukey´s test (α=0.05). Specimens filled with AH Plus had higher bond strength, followed by MTA Fillapex and Endofill (p<0.05). For light-curing unit, LED-1500 presented superior bond strength than LED-800, which was higher than QTH-600 (p<0.05). The cervical region had the greatest mean values (p<0.05) while apical part showed the lowest bond strength (p<0.05). CLMS revealed remaining filling material in the dentinal tubules for all groups. The eugenol-containing sealer (Endofill) compromised the push-out bond strength of composite resin to the root dentin. Bond strength was favored in the cervical region, and when LED-1500 was used.

Resumo O objetivo neste estudo foi avaliar a influência do cimento endodôntico e da fonte de luz fotoativadora na resistência de união (RU) regional da resina composta às raízes fragilizadas. Noventa raízes de incisivos foram experimentalmente fragilizados, submetidos ao preparo biomecânico e obturadas com Endofill, AH Plus ou MTA Fillapex. Os canais foram desobturados e reforçados com pinos de fibra de vidro e resina composta fotoativada com uma das fontes de luz: halógena a 600 mW/cm2 (QTH-600), diodo emissor de luz a 800 mW/cm2 (LED-800) e LED a 1500 mW/cm2 (LED-1500). As raízes foram seccionadas em slices provenientes dos terços cervical, médio e apical das regiões da raiz reforçada e analisadas por meio do teste de push out, microscopia eletrônica de varredura (MEV) e microscopia confocal de varredura a laser (MCVL). Os dados de resistência de união foram analisados por ANOVA a três critérios e teste de Tukey (α=0,05). Os espécimes obturados com AH Plus apresentaram maior resistência de união, seguido do MTA Fillapex e do Endofill (p<0,05). Para fonte de luz fotoativadora, LED-1500 apresentou resistência de união superior ao LED-800 que foi maior que QTH-600 (p<0,05). A região cervical obteve as maiores médias (p<0,05), enquanto que a região apical apresentou a menor resistência de união (p<0,05). MCVL revelou remanescente de material endodôntico nos túbulos dentinários para todos os grupos. O cimento contendo eugenol (Endofill) comprometeu a resistência de união da resina composta à dentina radicular. A resistência de união foi favorecida na região cervical, e quando o LED-1500 foi empregado.

1064-nm Nd: YAG and 980-nm Diode Laser EDTA Agitation on the Retention of an Epoxy-Based Sealer to Root Dentin

Abstract Root canal irrigants are used to minimize the negative effects of smear layer on endodontic sealer retention. The aim of this study was to evaluate the efficacy of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with ultrasonic, 1064-nm Nd:YAG and 980-nm diode laser on the retention of an epoxy-based sealer to the root canal walls. Forty single-rooted bovine teeth were instrumented with ProTaper rotary system and divided into four groups according to the final irrigation protocol (n = 10): (1) 17% EDTA (control); (2) 17% EDTA with 50-s ultrasonic agitation; (3) 17% EDTA with 50-s diode laser (2-W) agitation; and (4) 17% EDTA with 50-s Nd:YAG (1.5-W) laser agitation. After endodontic filling with gutta-percha F5 master cone and Sealer 26, the roots were sectioned at the cervical, middle, and apical root thirds to obtain 1.5-mm slices. Push-out tests were performed using a universal testing machine at a 1 mm/min crosshead speed. Data were analyzed using two-way ANOVA and Tukey's tests (α=0.05). Apical root thirds had significant higher retention values than cervical and middle thirds (p < 0.05). EDTA with 1064-nm Nd:YAG or 980-nm diode laser presented the highest retention values and was significantly different from EDTA with ultrasonic agitation and EDTA only (p < 0.05). Adhesive failures were predominant to EDTA only group. Mixed failures were predominant to all agitation groups. 1064-nm Nd:YAG and 980-nm diode laser EDTA agitation enhanced the retention of the epoxy-based sealer to the root canal walls compared with that due to EDTA only or EDTA with ultrasonic agitation.

Resumo Irrigantes para canais radiculares são usados para minimizar os efeitos negativos da camada de smear na retenção do cimento obturador. O objetivo deste estudo foi avaliar a eficácia da agitação do ácido etilenodiaminotetracético a 17% (EDTA) com ultrassom, Nd:YAG 1064-nm e laser diodo 980-nm na retenção de um cimento obturador à base de resina epóxica nas paredes do canal radicular. Quarenta dentes bovinos unirradiculares foram instrumentados com o sistema rotatório ProTaper e divididos em quatro grupos de acordo com o protocolo de irrigação final (n = 10): (1) EDTA 17% (controle); (2) EDTA 17% com agitação ultrassônica por 50-s; (3) EDTA 17% com agitação com laser diodo (2-W) por 50-s; e (4) EDTA 17% com agitação com laser Nd:YAG (1,5-W) por 50-s. Após obturação endodôntica com cone principal F5 e cimento Sealer 26, as raízes foram seccionadas nos terços radiculares cervical, médio e apical para obtenção de slices de 1,5-mm. Testes de push-out foram realizados utilizando uma máquina universal de ensaios com velocidade de carga de 1 mm/min. Os dados foram analisados utilizando os testes two-way ANOVA e Tukey's (α=0,05). Os terços radiculares apicais tiveram força de adesão significantemente maior que os terços cervical e médio (p<0,05). EDTA com Nd:YAG 1064-nm ou laser diodo 980-nm apresentaram os maiores valores de força de adesão e foram significantemente diferentes do EDTA com agitação ultrassônica e EDTA apenas (p < 0,05). Falhas adesivas foram predominantes apenas no grupo EDTA. Falhas mistas foram predominantes em todos os grupos de agitação. A agitação do EDTA com Nd:YAG 1064-nm e laser diodo 980-nm aumentou a força de adesão do cimento à base de resina epóxica às paredes do canal radicular comparado com a obtida com EDTA apenas ou EDTA com agitação ultrassônica.

Bonding Effectiveness of Universal Adhesive to Intracoronal Bleached Dentin Treated with Sodium Ascorbate

Abstract This study evaluated the effect of restorative protocol with sodium ascorbate on the shear bond strength (SBS) of a universal adhesive to intracoronal bleached dentin. One hundred-and-twenty bovine dentin fragments were randomly divided into 12 groups (n=10), according to the bleaching procedure (unbleached and bleached) and restorative protocol (no treatment, 10% sodium ascorbate -10SA, 35% sodium ascorbate -35SA and two-step etch-and-rinse -ER or one-step self-etch -SE Scotchbond universal adhesive approaches). Four whitening sessions were performed using 35% hydrogen peroxide. The samples from control groups were kept in relative humidity at 37 °C. Immediately after bleaching procedures, the assigned antioxidant solution was applied on dentin and restorative procedures were performed following either the ER or the SE approach. After 24 h, the specimens were subjected to SBS test. Data (MPa) were analyzed by ANOVA and Tukey's test (?=0.05). Lower SBS values were found for bleached specimens (8.54 MPa) compared with those unbleached (12.13 MPa) (p<0.05). The bond strength of the sodium ascorbate-treated groups was higher than those untreated, regardless of the strategy employed (p<0.05). Groups restored without sodium ascorbate showed lower bond strength values for both ER (8.32 MPa) and SE (8.28 MPa) adhesive strategies. The group treated with 10SA submitted to ER approach (10.14 MPa) was similar to untreated groups (p>0.05). It may be concluded that bond strength of composite resin to intracoronal dentin was affected by restorative protocol and reduced by bleaching.

Resumo Este estudo avaliou o efeito do protocolo restaurador empregando ascorbato de sódio na resistência ao cisalhamento do adesivo universal à dentina intracoronária clareada. Cento e vinte fragmentos de dentina bovina foram aleatoriamente divididos em doze grupos (n=10), de acordo com o procedimento clareador (clareados e não clareados) e protocolo restaurador (sem tratamento, ascorbato de sódio 10% (10AS), ascorbato de sódio (35AS) e estratégia de condicionamento total de dois passos (ER) ou estratégia autocondicionante de um passo (SE) com o sistema adesivo Scotchbond universal. Quatro sessões de clareamento foram realizadas empregando peróxido de hidrogênio a 35%. Os espécimes do grupo controle foram mantidos em umidade relativa a 37 °C. Imediatamente após os procedimentos de clareamento, as soluções antioxidantes selecionadas foram empregadas na dentina e os procedimentos restauradores foram realizados seguindo as estratégias ER ou SE. Após 24 h, os espécimes foram submetidos ao teste de resistência ao cisalhamento. Os dados (MPa) foram analisados pela ANOVA e teste de Tukey (?=0,05). Os menores valores de resistência ao cisalhamento foram encontrados para os espécimes clareados (8,54 MPa) comparados com aqueles não clareados (12,13 MPa) (p<0,05). A resistência de união dos grupos tratados com ascorbato de sódio foi maior que aqueles não tratados (p<0,05), independentemente da estratégia empregada. Grupos restaurados sem ascorbato de sódio demonstraram menores valores de resistência de união para ambas as estratégias adesivas ER (8,32 MPa) e SE (8,28 MPa) (p<0,05). O grupo tratado com ascorbato de sódio a 10% submetido à estratégia ER (10,14 MPa) foi similar ao não tratado (p>0,05). Pode ser concluído que a resistência de união da resina composta à dentina intracoronária foi afetada pelo protocolo restaurador e reduzida pelo clareamento.

Rehabilitation of weakened premolars with a new polyfiber post and adhesive materials.

Background: Polyfiber posts used inside the root canal can help to restore the fracture resistance of weakened premolars. Aim: To assess the fracture resistance of endodontically treated premolars restored with different techniques, including the new polyfiber post (Spirapost). Materials and Methods: One hundred superior premolars were distributed into 10 groups (n = 10): Sound teeth (G1‑positive control) and experimental (G2 to G10), which received MODP cavities and canal treatment. Groups were restored as follows: G2 ‑ unrestored (negative control); G3 ‑ microhybrid resin (MR); G4 ‑ flowable resin (FR) + (MR); G5 ‑ glass fiber post (Reforpost) + MR; G6 ‑ Reforpost + FR + MR; G7 ‑ polyethylene fiber (Ribbond) + MR; G8 ‑ Ribbond + FR + MR; G9 ‑ polyfiber post (Spirapost) + MR and G10 ‑ Spirapost + FR + MR. After 24 h, the specimens were loaded until fracture. Data were analyzed by ANOVA and Tukey’s test (P < 0.05). Results: Premolars restored with Spirapost (G9 and G10) provided the highest fracture strength (P < 0.05), similar to sound teeth (G1), regardless of the composite resin. Intermediate values were achieved by G3, G4, G5, G6, G7, and G8, which were similar (P > 0.05) and different from the others (P < 0.05). Inferior values were found in G2 (P < 0.05). Conclusion: Fracture resistance of premolars with MODP cavities and endodontic access was recovered with the direct rehabilitation with Spirapost, regardless of the type of composite resin.

Impact of Intracoronal Dentin Treatment Prior to Bleaching on Bond Strength of Restorative Materials

Surface treatment of dentin before the bleaching procedure may affect its permeability and influence the bond strength of restorative materials. This study evaluated the influence of surface treatment before the bleaching on shear bond strength (SBT) of restorative materials to intracoronal dentin. Dentin slabs were subjected to surface treatment: no bleaching (control - CON), no surface treatment + bleaching (HP), 37% phosphoric acid + bleaching (PA) and Er:YAG laser + bleaching (L). After the bleaching procedure, specimens (n=10) were restored with: microhybrid composite resin (MH), flowable composite resin (F), and resin-modified glass-ionomer cement (RMGIC). The shear test was carried out. ANOVA and Tukey's test (α=0.05) showed significant difference for surface treatment and restorative materials (p<0.05). CON presented higher STB and was statistically different from HP (p<0.05). PA and L showed intermediate values and were statistically similar to CON and HP (p>0.05). STB for MH and F were higher than RMGIC (p<0.05), and did not differ from each other (p>0.05). The surface treatments with phosphoric acid and Er:YAG laser before the bleaching procedure provided shear bond strength at the same level of unbleached dentin and the composite resins presented superior bond strength to the intracoronal dentin.

O tratamento superficial da dentina previamente ao clareamento pode afetar a sua permeabilidade e influenciar a resistência de união de materiais restaurados. Este estudo avaliou a influência do tratamento superficial antes do clareamento na resistência ao cisalhamento (RC) de materiais restauradores à dentina intracoronária. Fragmentos de dentina foram submetidos ao tratamento de superfície: não clareadas (controle - CON), sem tratamento de superfície + clareamento (HP), ácido fosfórico 37% + clareamento (AF), e laser Er:YAG + clareamento (L). Após o procedimento clareador, os espécimes foram restaurados com (n=10): resina composta micro-híbrida (MH), resina composta fluida (F), e cimento de ionômero de vidro modificado por resina (CIVMR). O teste de cisalhamento foi realizado. ANOVA e teste de Tukey (α=0,05) mostraram diferença significante para tratamento superficial e material restaurador (p<0,05). O grupo controle apresentou maior resistência de união e foi estatisticamente diferente de HP (p<0,05). AF e L mostraram valores intermediários e foram similares ao CON e HP (p>0,05). A resistência de união para MH e F foi maior que CIVMR (p<0,05), e não diferiram entre si (p>0,05). O tratamento da superfície dentinária com ácido fosfórico e laser Er:YAG previamente ao clareamento promoveu resistência de união ao nível da dentina não clareada e a adesão à dentina intracoronária foi superior com as resinas compostas.

Ultra-thin porcelain laminates to restore esthetics of anterior teeth: case report

Introduction: The ultra-thin porcelain laminates provide the esthetic harmony to the smile compromised by the presence of diastema between maxillary incisors. Objective: To report the dental aesthetic recovery with ultra-thin porcelain laminates, so-called "contact lenses". Case report: Patient sought treatment reporting presence of diastema between the anterior teeth. After the clinical examination, impressions were made to obtain study models and diagnostic wax-up. Home bleaching was conducted using 10% carbamide peroxide for 21 days. Next, the mock-up with bisacrylic self-curing composite resin and the functional impression were conducted. For cementation, dental surfaces were etched with 37% phosphoric acid followed by applying the adhesive system. The resin cement was inserted within internal part of the contact lenses previously treated with hydrof luoric acid and silane, and the prosthetic samples were positioned over the labial surfaces of the anterior teeth. After light-curing, the finishing procedure was performed. Conclusion: Ultra-thin porcelain laminates (contact lenses) were viable, efficient, and conservative procedures for recovering dental esthetic, with no need of invasive procedures.

Influence of Apical Enlargement in Cleaning of Curved Canals Using Negative Pressure System

This study aimed to evaluate, by scanning electron microscopy (SEM), the cleaning of canal walls with moderate curvature subjected to biomechanical preparation with different final diameters using apical negative pressure irrigation. Thirty-two mesiobuccal roots of molars were divided into 4 groups (n=8) according to the instrument's final diameter: GI: 30.02, GII: 35.02, GIII: 40.02 and GIV: 45.02. Irrigating procedure was performed at each change of instrument with 1% NaOCl using the Endovac system. Final irrigation was conducted with 17% EDTA for 5 min. The SEM photomicrographs were evaluated under 35× and 1000× magnification, by three calibrated examiners, in a double-blind design. Data were submitted to Kruskal-Wallis and Dunn's post hoc tests (α=0.05). Canals instrumented with 30.02 and 35.02 final diameters showed more debris, statistically different from the other groups (p<0.05). Comparing each root canal third, for the cervical and apical portions no statistically significant difference (p>0.05) was found among the four groups. Regarding the presence of smear layer, canals with 30.02 final diameter showed the highest scores, statistically different from the 45.02 group (p<0.05) and similar to the 35.02 and the 40.02 groups (p>0.05). Although none of the studied diameters completely removed debris and smear layer, it may be concluded that instrumentation with higher final diameters was more effective in cleaning the root canals with moderate curvature.

Este estudo buscou avaliar, por meio de microscopia eletrônica de varredura (MEV), a limpeza das paredes de canais com curvatura moderada, submetidos ao preparo biomecânico com diferentes diâmetros finais utilizando-se irrigação por pressão apical negativa. Trinta e duas raízes mésio-vestibulares de molares foram divididas em 4 grupos (n=8) de acordo com o diâmetro final dos instrumentos: GI: 30.02, GII: 35.02, GIII: 40.02 e GIV: 45.02. O procedimento de irrigação foi realizado a cada troca de instrumento com NAOCl 1% utilizando o sistema EndoVac. A irrigação final foi conduzida com EDTA 17% por 5 min. As microfotografias de MEV foram avaliadas sob aumentos de 35× e 1000×, por três examinadores calibrados, em estudo duplo-cego. Os dados foram submetidos ao teste de Kruskal-Wallis e pós-teste de Dunn (=0,05). Os canais instrumentados com diâmetros finais de 30.02 e 35.02 demonstraram mais debris, estatisticamente diferente dos demais grupos (p<0,05). Comparando-se cada terço do canal radicular, para as porções cervical e apical não foi encontrada diferença estatisticamente significante (p>0,05) entre os quatro grupos. Com relação à presença de smear layer, canais com diâmetro final de 30.02 demonstraram os maiores scores, estatisticamente diferente do grupo 45.02 (p<0,05) e similar aos grupos 35.02 e 40.02 (p>0,05). Apesar de nenhum dos diâmetros estudados ter removido completamente os debris e a smear layer, pode ser concluído que a instrumentação com diâmetros finais maiores foi mais efetiva na limpeza dos canais radiculares com curvatura moderada.

Effect of Light Sources on the Bond Strength of Resin Material to Thin-walled Roots

The aim of this study was to evaluate the bond strength to the dentin of an adhesive material used for root reinforcement light activated with different sources. Roots were divided into 4 groups (n=15) according to the light source used to activate the resin reinforcement: GI, non-weakened roots (control); GII, halogen light (H) 600 mW/cm2; GIII, LED 800 mW/cm2 and GIV, LED 1500 mW/cm2. The reinforcement was done with adhesive, composite resin and fiberglass posts. After 24 h, the specimens were sectioned and the first slice of each post region was used in the push out test in a universal testing machine with a crosshead speed of 0.5 mm/min. Failure modes of the debonded specimens were examined. Data (MPa) were analyzed by ANOVA and Holm-Sidak test (=0.05). The second slice from each region was analyzed by scanning electron microscopy (SEM). LED-1500 (4.69 ± 1.74) provided bond strength similar to the control group (5.05 ± 2.63) and statistically different from H-600 (1.96 ± 0.94) and LED-800 (2.75 ± 1.90), which were similar to each other (p<0.05). Cervical (4.16 ± 2.32) and middle (4.43 ± 2.32) regions showed higher bond strength than the apical (2.25 ± 1.50) (p<0.05). There was a prevalence of adhesive failures in H-600 and LED-800 and cohesive failures in LED-1500. SEM showed the formation of long, numerous and fine tags. It was concluded that LED-1500 provided higher bond strength of resin reinforcement to the dentin.

O objetivo deste estudo foi avaliar a resistência de união à dentina de uma resina utilizada para reforço de raiz, ativada com diferentes fontes de luz. De acordo com a fonte de luz utilizada as raízes foram divididas em 4 grupos (n = 15): GI, raízes não fragilizadas (controle); GII, luz halógena (H) 600 mW/cm2; GIII, LED 800 mW/cm2 e GIV, LED 1500 mW/cm2. O reforço foi feito com adesivo, resina composta e pino de fibra de vidro. Após 24 h, os espécimes foram seccionados e o primeiro slice de cada região utilizado para o teste de união push out, na máquina de ensaios universais com 0,5 mm/min, e o tipo da falha avaliada. Os dados obtidos (MPa) foram analisados utilizando os testes de ANOVA e Holm-Sidak (=0.05). O segundo slice de cada região foi analisado por microscopia eletrônica de varredura (MEV). O LED-1500 (4.69 ± 1.74) proporcionou resistência a união similar ao controle (5.05 ± 2.63) e estatisticamente diferente do H-600 (1.96 ± 0.94) e LED-800 (2.75 ± 1.90), que são similares entre si (p<0.05). As regiões cervical (4.16 ± 2.32) e média (4.43 ± 2.32) apresentaram alta resistência à união quando comparadas à região apical (2.25 ± 1.50) (p<0.05). Houve uma predominância de falhas adesivas com as fontes de luzes H-600 e LED-800 e coesivas com o LED-1500. A análise em MEV demonstrou a formação de longos tags resinosos. Desta forma, pode-se concluir que o LED-1500 proporcionou maior resistência à resina utilizada para o reforço da dentina radicular.

Tensile Strength of Glass Fiber Posts Submitted to Different Surface Treatments

The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.

O objetivo deste estudo in vitro foi avaliar a resistência à tração de pinos de fibra de vidro submetidos a diferentes tratamentos de superfície. Quarenta e oito caninos superiores tiveram suas coroas seccionadas e as raízes tratadas endodonticamente. As raízes foram incluídas em resina acrílica e distribuídas em 3 grupos de acordo com o tratamento de superfície aplicado aos pinos: Grupo I: os pinos receberam agente silano por 30 s e adesivo; Grupo II: os pinos foram limpos com álcool e então receberam o agente silano e adesivo; Grupo III: os pinos foram submetidos ao condicionamento com ácido fosfórico a 37% por 30 s, seguido de agente silano e adesivo. Cada grupo foi dividido em 2 subgrupos de acordo com fotoativação do adesivo antes da inserção do pino no interior do canal: A – adesivo não foi fotoativado, B: o adesivo foi fotoativado. Todos os pinos foram cimentados com Panavia F e as amostras foram submetidas a teste de tração utilizando máquina universal de ensaios, com velocidade de 1 mm/min. Os dados obtidos foram submetidos à ANOVA a um critério e ao teste de Tukey com nível de significância de 5%. Houve diferença estatisticamente significante (p<0,01) entre o grupo GIII-B e os grupos GI-A e GI-B. Os demais grupos não apresentaram diferenças significantes entre si (p>0,05). Pode-se concluir que as substâncias utilizadas para a limpeza dos pinos interferiram em sua retenção, independente da fotopolimerização do adesivo.

Bond strength of dual-cured resin cements to root canal dentin

Introduction: The bonding of dental posts to the root canal walls depends on the resin cement Objective:This in vitro study assessed the bond strength of resin cements used for post cementation to different root regions. Material and methods: Thirty canine roots were endodontically treated and prepared to receive dental posts which were luted with different resin cements (n = 10): Enforce (Dentsply), Panavia F (Kuraray Dental Co) and RelyX ARC (3M ESPE). The cements were light-cured for 20 s. After cementation, slices from cervical, middle and apical post/root regions were submitted to the push out test in a universal testing machine. The data (MPa) were analyzed using ANOVA and Tukey’s test (a = 0.05). Results: RelyX ARC (3.24 ± 1.49) and Enforce (3.45 ± 1.42) showed higher bond strength than Panavia (0.95 ± 0.39) (p < 0.05), without statistically significant difference between each other (p > 0.05). The bond strength values at the cervical (3.37 ± 1.47) were higher than middle (2.62 ± 1.94) and apical (1.65 ± 0.99) regions (p < 0.05), which were similar between them (p > 0.05). Conclusion: The resin cements RelyX ARC and Enforce presented greater bond strength than Panavia and the bond strength was higher at the cervical region.

Effect of light-activation with different light-curing units and time intervals on resin cement bond strength to intraradicular dentin

The aim of this study was to assess the bond strength of a resin cement to intraradicular dentin varying the light-curing unit and the moment at which the light was applied. Post spaces of endodontically treated canines were prepared. The roots were distributed into 6 groups (n=10) according to the light-curing unit and the moment of light exposure: I) Quartz tungsten halogen-600 mW/cm² (QTH) + immediate light activation (t0); II) QTH + light activation after 10 min (t10); III) Light-emitting diodes (LED)-800 mW/cm² (LED-800)+ t0; IV) LED-800 + t10; V) LED-1,500 mW/cm² (LED-1500)+ t0; VI) LED-1500 + t10. After post cementation, slices from coronal, middle and apical post/root regions were submitted to the push-out test and failure evaluation. It was verified that LED-800 (4.40 ± 3.00 MPa) and LED-1500 (4.67 ± 3.04 MPa) provided bond strength statistically superior to QTH (3.13 ± 1.76 MPa) (p<0.05), and did not differ from each other (p>0.05). There was no significant difference between t0 and t10 (p>0.05). Coronal post/root region (4.75 ± 3.10 MPa) presented significantly higher bond strength than the apical (3.32 ± 2.30 MPa) (p<0.05) and middle regions (4.14 ± 2.99 MPa) showed intermediate values. Adhesive failures were predominant when using QTH. Adhesive and mixed failures occurred more frequently in the apical region. Higher adhesion of the resin cement to intraradicular dentin was observed in the coronal region with LED light-activation, regardless of the moment of light exposure.

O objetivo deste estudo foi avaliar a resistência de união do cimento resinoso à dentina intrarradicular em função da fonte fotoativadora e do momento de aplicação da luz. Os espaços para cimentação dos pinos foram preparados em caninos tratados endodonticamente. As raízes foram distribuídas em seis grupos (n = 10) de acordo com a fonte fotoativadora e momento de exposição à luz: I) Luz halógena (LH) com densidade de potência 600 mW/cm² + fotoativação imediata (t0); II) LH + fotoativação após 10 min (t10); III) LED com densidade de potência 800 mW/cm² (LED-800)+ t0; IV) LED-800 + t10; V) LED com densidade de potência 1.500 mW/cm² (LED-1500)+ t0; VI) LED-1500 + t10. Após a cimentação dos pinos, slicesdas regiões cervical, média e apical foram submetidos ao teste de push-out e avaliação das falhas. Verificou-se que LED-800 (4,40 ± 3,00 MPa) e LED-1500 (4,67 ± 3,04 MPa) proporcionaram resistência de união estatisticamente superior à LH (3,13 ± 1,76 MPa) (p<0,05), e não diferiram entre si (p>0,05).Não houve diferença estatisticamente significante da resistência de união entre t0 e t10 (p>0,05). A região cervical (4,75 ± 3,10 MPa) apresentou maiores valores de resistência de união que a apical (3,32 ± 2,30 MPa) (p<0,05) e a região média (4,14 ± 2,60 MPa) mostrou valores intermediários. Falhas adesivas foram predominantes no grupo LH, independentemente da região pino/canal. A parte apical apresentou predomínio de falhas adesivas e mistas. Concluiu-se que a resistência de união do cimento resinoso à dentina intrarradicular foi maior no terço cervical,com fotoativação com LED, independente do momentode exposição à luz.

Flexural properties, morphology and bond strength of fiber-reinforced posts: influence of post pretreatment

The aim of this study was to assess the influence of surface pretreatments of fiber-reinforced posts on flexural strength (FS), modulus of elasticity (ME) and morphology of these posts, as well as the bond strength (BS) between posts and core material. Fifty-two fiber posts (smooth and serrated) were assigned to 4 groups (n=13): no treatment (control), 10% hydrogen peroxide (HP) for 10 min (HP-10), 24% HP for 1 min (HP-24) and airborne-particle abrasion (Al2O3). To evaluate FS and ME, a 3-point bending test was performed. Three posts of each group were examined by scanning electron microscopy. Composite resin was used as the core build-up and samples were sectioned to obtain microtensile sticks. Data were analyzed by ANOVA and Tukey's test (α=0.05). For FS, significant differences were observed between posts type and surface pretreatment (p<0.05), with the highest means for the smooth posts. Al2O3 provided higher FS than HP-24. Al2O3 promoted higher ME than HP-24 and control. SEM images revealed partial dissolution of the resin matrix in all treated groups. The smooth posts had higher BS and FS than serrated posts (p<0.05). Mechanical properties of the glass fiber posts and the bond strength between posts and composite material were not altered by the surface treatments, except for airborne-particle abrasion that increased the post elastic modulus.

O objetivo deste estudo foi avaliar a influência do pré-tratamento de superfície dos pinos de fibra de vidro na resistência à flexão (RF), módulo de elasticidade (ME) e morfologia, bem como a resistência de união (RU) entre os pinos e o núcleo de preenchimento. Cinqüenta e dois pinos de fibra de vidro (lisos e serrilhados) foram divididos em 4 grupos (n=13): sem tratamento (controle), peróxido de hidrogênio a 10% por 10 min (HP-10), peróxido de hidrogênio 24% por 1 min (HP-24) e jato de óxido de alumínio (Al2O3). Para avaliar a RF e ME, o ensaio de flexão de 3 pontos foi realizado. Três pinos de cada grupo foram examinados em MEV. Resina composta foi utilizada como núcleo de preenchimento e as amostras foram seccionadas para obter palitos de microtração. Os dados foram analisados por ANOVA e teste de Tukey (α=0,05). Na RF, observou-se diferença estatisticamente significante entre os pinos e tipo de pré-tratamento de superfície (p<0,05), com as maiores médias para os pinos lisos. Al2O3 proporcionou maior RF que HP-24. Al2O3 promoveu maior ME que HP-24 e grupo controle. MEV revelou dissolução parcial da matriz de resina em todos os grupos tratados. Os pinos lisos tiveram a maior RU (p<0,05). Os pinos lisos apresentaram RF e RU superior aos pinos serrilhados (p<0,05). As propriedades mecânicas dos pinos de fibra de vidro e a resistência de união entre os pinos e o material resinoso não foram alterados pelos tratamentos de superfície, com exceção do jato de óxido de alumínio que aumentou o módulo de elasticidade dos pinos.

Estratégias para prevenção e controle da erosão dental / Strategies for prevention and control of dental erosion

Devido ao aumento da incidência e prevalência da erosão dental, torna-se importante abordar e discutir sua etiopatogenia e tratamento. Para preservar ao máximo a estrutura dental, é essencial que o profissional da área odontológica esteja apto para detectar os fatores e os comportamentos de risco, diagnosticar as lesões em estágios iniciais e instituir estratégias preventivas contra a formação de novas lesões e de controle da progressão daquelas já presentes. É fundamental que o conceito de erosão dental, os fatores etiológicos que podem estar envolvidos no processo patológico e as possíveis interações com outros fenômenos de desgaste sejam esclarecidos. Dessa forma, o objetivo desta revisão é apresentar a definição e a etiologia da erosão dental e discutir possíveis estratégias de tratamento e seus mecanismos de ação na prevenção e no controle do desenvolvimento da erosão dental.

Objetivo Owing to the increased incidence and prevalence of dental erosion, it is important to broach and discuss its etiopathogenesis and management. For maximal preservation of dental structures, practitioners must be able to recognize risk factors and behaviors for dental erosion, diagnose initial lesions and implement preventive and interceptive strategies. Therefore, clarification of dental erosion, its likely etiology and interactions with other wear process are of outmost relevance. The aims of this literature review paper are: to present the definition and etiology of dental erosion and to discuss strategies and their mechanism of action in preventing and controlling dental erosion.

Effect of bleaching protocols with 38 percent hydrogen peroxide and post-bleaching times on dentin bond strength

This study assessed the effect of bleaching protocols with 38 percent hydrogen peroxide (HP) and post-bleaching times on shear bond strength of a composite resin to dentin. One-hundred slabs of intracoronary dentin were included and randomly assigned into 2 groups according to the bleaching protocol: HP (2 applications of 10 min each) and HP activated by LED laser (2 applications of 10 min each/45 s of light activation). Groups were subdivided according to the post-bleaching time (n=10): 1 day, 3 days, 7 days, 10 days and 14 days. The control group was unbleached and restored (n=10). The specimens were restored with Single Bond adhesive system/Filtek Z250 resin using a polytetrafluorethylene matrix and were submitted to the shear bond strength testa after 24 h,. Data were analyzed by ANOVA and Tukey's test (α=0.05). Unbleached group (0.283 ± 0.134) had the highest bond strength and was statistically similar (p>0.05) to HP/10 days (0.278 ± 0.064), HP + LED laser/10 days (0.280 ± 0.078), HP/14 days (0.281 ± 0.104), HP + LED laser/14 days (0.277 ± 0.093). Lower bond strength were verified in HP/1 day (0.082 ± 0.012), HP/3 days (0.079 ± 0.013), HP + LED laser/1 day (0.073 ± 0.018) and HP + LED laser/3 days (0.080 ± 0.015), which were statistically similar (p>0.05). HP/7 days (0.184 ± 0.154) and HP + LED laser/7 days (0.169 ± 0.102) had intermediate values (p<0.05). The restorative procedure of intracoronary dentin bleached with 38 percent HP with or without the use of light source should be performed after at least 10 days after the bleaching treatment.

Este estudo avaliou o efeito de protocolos de clareamento com peróxido de hidrogênio 38 por cento (PH) e tempos pós-clareamento na resistência ao cisalhamento de uma resina composta á dentina. Cem fragmentos de dentina intracoronária foram incluídos e distribuídos aleatoriamente em 2 grupos experimentais de acordo com o protocolo de clareamento: PH (2 aplicações de 10 min cada) e HP ativado por LED laser (2 aplicações de 10 min cada/45 s de ativação pela luz). Os grupos foram subdivididos de acordo com o tempo pós-clareamento (n=10): 1 dia, 3 dias, 7 dias, 10 dias e 14 dias. O grupo controle não foi clareado e apenas restaurado (n=10). Os espécimes foram restaurados com sistema adesivo Single Bond/resina Filtek Z250 usando matriz de teflon. Após 24 h, foram submetidos ao teste de cisalhamento. Os dados foram analisados por ANOVA e teste de Tukey (α=0,05). O grupo não clareado (0,283 ± 0,134) apresentou a maior resistência de união e foi estatisticamente semelhante (p>0,05) ao PH- 10 dias (0,278 ± 0,064), PH + LED laser/10 dias (0,280 ± 0,078), PH/14 dias (0,281 ± 0,104), PH + LED laser/14 dias (0,277 ± 0,093). Resistência de união inferior foram verificadas para PH/1 dia (0,082 ± 0,012), PH/3 dias (0,079 ± 0,013), PH + LED laser/1 dia (0,073 ± 0,018) e PH + LED laser/3 dias (0,080 ± 0,015), que foram estatisticamente semelhantes entre si (p>0,05). HP/7 dias (0,184 ± 0,154) e PH + LED laser/7 dias (0,169 ± 0,102) apresentaram valores intermediários (p<0,05). O procedimento restaurador da dentina intracoronária clareada com peróxido de hidrogênio 38 por cento, com ou sem o uso de fonte de luz, deve ser realizado pelo menos após 10 dias do tratamento clareador.

Apical microleakage and SEM analysis of dentin surface after 980 nm diode laser irradiation

This study evaluated the effect of 980-nm diode laser on apical microleakage and intraradicular dentin morphology. Roots of 110 mandibular incisors were used in the study: 92 for microleakage test and 18 for scanning electron microscopy (SEM). Roots were randomly assigned to 3 groups according to the irrigating solution (water, NaOCl and NaOCl/EDTA) and were divided into 3 subgroups according to the laser irradiation protocol (without irradiation, irradiated at 1.5 W and irradiated at 3.0 W). Two specimens of each subgroup were prepared for SEM. The remaining roots were filled with AH Plus and gutta-percha. Apical leakage was assessed by ink penetration and data were analyzed statistically by ANOVA and Tukey-Krammer test (α=0.05). SEM analysis showed intensification of changes with increase of laser power as well as variations according to the irrigating solution. Modified smear layer was observed in specimens treated with water and irradiated with laser. Roots irrigated with NaOCl/EDTA had lower levels of infiltration (0.17 ± 0.18 mm) differing significantly (p<0.05) from those of roots irrigated with water (0.34 ± 0.30 mm), but similar (p>0.05) to those irrigated with NaOCl (0.28 ± 0.29 mm). Non-irradiated roots had lower levels of infiltration (0.10 ± 0.14 mm), differing (p<0.05) from those irradiated at 1.5 W (0.32 ± 0.22 mm) and 3.0 W (0.37 ± 0.32 mm). The 980 nm diode laser modified dentin morphology and increased apical microleakage.

Este estudo avaliou o efeito do laser de diodo 980 nm na microinfiltração apical e na morfologia intrarradicular da dentina. Raízes de 110 incisivos inferiores foram utilizadas no estudo: 92 para o teste de microinfiltração e 18 para microscopia eletrônica de varredura (MEV). As raízes foram divididas em 3 grupos de acordo com a solução irrigante (água, NaOCl e NaOCl/EDTA) e subdivididas em 3 de acordo com a irradiação laser (sem irradiação, irradiados com 1,5 W e irradiados com 3,0 W). Duas amostras de cada subgrupo foram preparadas para MEV. As raízes restantes foram preenchidas com AH Plus e guta percha. A infiltração apical foi avaliada nas raízes por meio da penetração do corante e os dados foram analisados por ANOVA e teste de Tukey-Krammer (α=0,05). Os resultados da MEV mostraram intensificação das mudanças quando se aumentou a potência do laser e variações de acordo com a solução irrigadora. Camada de smear modificada foi observada em espécimes tratados com água e irradiados com laser. Raízes irrigadas com NaOCl/EDTA tiveram níveis menores de infiltração (0,17 ± 0,18 mm) estatisticamente diferente (p<0,05) das raízes irrigadas com água (0,34 ± 0,30 mm), mas semelhante (p>0,05) aos irrigados com NaOCl (0,28 ± 0,29 mm). As raízes não irradiadas tiveram níveis menores de infiltração (0,10 ± 0,14 mm), diferente (p<0,05) de 1,5 W (0,32 ± 0,22 mm) e 3.0 W (0,37 ± 0,32 mm). O laser de diodo 980 nm alterou a morfologia da dentina e aumentou a infiltração marginal apical.

Fracture resistance of teeth subjected to internal bleaching and restored with different procedures

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different procedures. Forty maxillary incisors were endodontically treated and assigned to 4 groups (n=10): G1- restored with composite resin (CR), G2- bleached with hydrogen peroxide (HP) and restored with CR, G3- restored with CR and fiberglass posts (CR + posts) and G4- bleached and restored with CR + posts. HP was applied in the buccal surface and pulp chamber 3 times at each one of 2 sessions with an interval of 7 days between them. Additional 10 sound incisors were subjected to fracture strength test (gold standard). The fracture strength (kN) was determined in an Instron machine. Data were analyzed by ANOVA and Tukey-Kramer test (α=0.05). The untreated teeth (gold standard) showed the highest (p<0.05) fracture strength (0.43 ± 0.16). Teeth restored with CR (G1) without internal bleaching had the lowest (p<0.05) fracture strength (0.23 ± 0.11). Teeth bleached and restored with CR (G2) (0.26 ± 0.10), restored with CR + posts ithout internal bleaching (G3) (0.31 ± 0.17) and, bleached and restored with CR + posts (G4) (0.33 ± 0.12) had intermediate values, sometimes similar to the group with the highest value, sometimes similar to the group with the lowest value. In conclusion, as far as the fracture strength is concerned, teeth subjected to internal bleaching can be restored with composite resin alone, as the use of posts in these teeth did not increase their resistance.

Este estudo avaliou a resistência à fratura de dentes submetidos ao clareamento interno restaurados com diferentes procedimentos. Quarenta incisivos superiores foram tratados endodonticamente e divididos em 4 grupos (n = 10): G1- restaurados com resina composta (RC), G2- clareados com peróxido de hidrogênio (PH) e restaurados com o RC, G3- restaurado com RC e pinos de fibra de vidro (RC + pinos) e G4- clareados e restaurados com RC + pinos. O PH foi aplicado na superfície vestibular e câmara pulpar 3 vezes por sessão, por 2 sessões com intervalo de 7 dias entre elas. Dez dentes hígidos adicionais foram submetidos a teste fratura (padrão ouro). A resistência à fratura (kN) foi determinada em máquina Instron. Os dados foram analisados por Análise de Variânica e teste de Tukey-Krammer (α= 0,05). Os dentes não tratados (padrão ouro) apresentaram a maior resistência à fratura (0,43 ± 0,16) (p <0,05). Os dentes restaurados com RC (G1) apresentaram a menor resistência à fratura (0,23 ± 0,11) (p <0,05). Os dentes clareados e restaurados com RC (G2) (0,26 ± 0,10), restaurado com RC + pinos (G3) (0,31 ± 0,17) e os clareados e restaurados com RC + pinos (G4) (0,33 ± 0,12) apresentaram valores intermediários, ora semelhantes ao do grupo com o maior valor, ora similares ao grupo de valores mais baixos. Pode-se concluir que os dentes submetidos ao clareamento interno podem ser restaurados com apenas resina composta.

Aspectos físico-químicos relacionados ao potencial erosivo de bebidas ácidas / Physicochemical aspects related to the erosive potential of acid beverages

O entendimento do papel dos aspectos físico-químicos relacionados ao caráter erosivo de bebidas ácidas contribui para fundamentar estratégias que visem minimizar a formação e progressão de lesões de erosão. Objetivo: Este trabalho visou revisar o papel de aspectos relacionados ao potencial erosivo de bebidas ácidas, esclarecendo como o tipo, concentração e propriedades quelantes do ácido que as compõem, pH, acidez titulável, conteúdo de cálcio, fosfato e flúor, presença de caseína, temperatura e adesividade das bebidas, influenciam, de forma isolada ou combinada, no des-gaste dental. Revisão de literatura: Realizada mediante pesquisa em indexadores internacional (Medline) e nacional (BBO) e em um livro. Buscaram-se evidências sobre o tema em artigos de investigação cientifica e de revisão de literatura. Considerações finais: Concluiu-se que: 1) o tipo e o potencial quelante do ácido, o pH, a acidez titulável, as concentrações de cálcio e fosfato, a temperatura e a adesividade das bebidas modulam seu potencial erosivo; 2) individualmente, o pH, acidez titulável e conteúdo de cálcio são os parâmetros que melhor revelam a capacidade das bebidas em propor-cionar a dissolução mineral da estrutura dental; 3) para uma caracterização mais precisa do potencial erosivo de bebidas ácidas, deve-se considerar a interação entre os diferentes aspectos físico-químicos.

Caracterização dos transtornos alimentares e suas implicações na cavidade bucal / Characterization of eating disorders and their implications in the oral cavity

Os dois principais transtornos alimentares evidenciados na clínica contemporânea são anorexia e bulimia nervosas. Entretanto, outras anormalidades do comportamento alimentar em que os critérios necessários para o diagnóstico de anorexia e bulimia não são preenchidos, recebem a denominação de transtorno alimentar "atípico", como o transtorno da compulsão alimentar periódica e a síndrome do comer noturno. Com o intuito de preservar a estrutura dental, minimizando os danos bucais, é indispensável que, inserido na equipe multiprofissional de tratamento desta patologia, o cirurgião-dentista possa diagnosticar as manifestações associadas especificamente aos determinados tipos de desordens alimentares. Detectar as lesões nos tecidos bucais em estágios iniciais, instituir estratégias preventivas contra o desenvolvimento de novas lesões e controlar a progressão daquelas já presentes contribui para o tratamento completo do indivíduo. Para isso, previamente à apresentação das manifestações bucais, é fundamental apresentar conceitos, características e sintomas específicos dos transtornos alimentares. Dessa forma, o objetivo desta revisão de literatura, desenvolvida a partir de referências bibliográficas encontradas através de pesquisa nas bases de dados Medline e Lilacs é apresentar características, sinais e sintomas dos transtornos alimentares e associar as suas manifestações na cavidade bucal. Concluiu-se que o dentista apresenta papel importante na detecção das manifestações bucais dos transtornos alimentares e pode auxiliar no diagnóstico dos distúrbios e no tratamento do indivíduo.

The two main eating disorders in the contemporary clinical practice are anorexia and bulimia nervosa. However, other disturbs of eating behavior, not diagnosed as anorexia and bulimia, are called "atypical" eating disorders such as binge eating disorder and night eating syndrome. Aiming to preserve the tooth structure minimizing the damages is essential that the dentist, inserted in the multidisciplinary team of treatment of eating disorders, diagnoses the manifestations associated to specific eating disorders. To detect lesions in the oral cavity in early stages, to institute preventive strategies against the development of new lesions and to control the progression of those already present contributes to the complete treatment of the individual. For that, prior to the presentation of the oral manifestations, it is crucial that concepts, characteristics and specific symptoms of eating disorders are descripted. The purpose of this review is to present the signs and symptoms of eating disorders and associate its manifestations in the oral cavity. For this, the data base Medline and Lilacs were accessed and relevant references were used. It was conclude that the dentist had important participation in the detection of the oral manifestations of eating disorders and may contributes to diagnosis the disturbs and to treat the patient.

Control of erosive tooth wear: possibilities and rationale

Dental erosion is a type of wear caused by non bacterial acids or chelation. There is evidence of a significant increase in the prevalence of dental wear in the deciduous and permanent teeth as a consequence of the frequent intake of acidic foods and drinks, or due to gastric acid which may reach the oral cavity following reflux or vomiting episodes. The presence of acids is a prerequisite for dental erosion, but the erosive wear is complex and depends on the interaction of biological, chemical and behavioral factors. Even though erosion may be defined or described as an isolated process, in clinical situations other wear phenomena are expected to occur concomitantly, such as abrasive wear (which occurs, e.g, due to tooth brushing or mastication). In order to control dental loss due to erosive wear it is crucial to take into account its multifactorial nature, which predisposes some individuals to the condition.